이규확
2011-04-07 20:24:41
3
1406
업무에 수고 많습니다.
아래는 NACE RP0472 Section 5.1 의 원본입니다.
5.1 ASME Boiler and Pressure Vessel Code, Section IX,
requires qualification of welding procedures to ensure that
room-temperature tensile strength and ductility of the
weldment meet minimum values. Welding must be
performed within the essential variables specified for the
welding process used. The ASME Boiler and Pressure
Vessel Code has no requirements for hardness testing
during procedure qualification tests. The following
practices for hardness testing during procedure
qualification tests have been developed and apply
primarily to weldments where PWHT or base material
chemistry controls are not used. The user shall specify
when this hardness testing is required and which of the
following practices are required, after reviewing the
intended service for the weldment.
이를 현장에 적용하는데, 어디까지 적용을 하는가가 관건입니다.
파란색글짜를 보시면, 적용예외사항이 나옵니다.
1) 열처리를 하는 경우와 2) base metal chemistry control 을 하지
않는 경우로 해석됩니다.
++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++
상황설명
PQR 시에 NACE RP 0472 Section 5 에 따라서 Hardness 를 하라고 해서 Hardness만을 따라 했고
(합격범위에 들었음), 기타 다른 조항은 ASME Section IX 를 따랐음.
사업주는 NACME RP 0472 Section 5에 따라서 PQR 을 다시 하라는 것입니다.
즉 Section 5.2.2 에 따라서 최대 CE 로 하라고 하고,
5.2.2 Maximum CE should not exceed the
corresponding values obtained on the test sample.
All chemical requirements should be applied to ladle
analyses, unless otherwise specified by the user.
그리고 Section 5.2.4 에 따라서 입열량을 제어하고
5.2.4 For all welding processes, the heat input
during production welding should not vary by more
than +25/-10% from the heat input used on the test
sample.
마지막으로 Section 5.2.7 에 따라 예열및 층간온도를 관리하라고 합니다.
5.2.7 Preheat and interpass temperatures used
during production welding should be greater than or
equal to that used in the welding procedure
qualification tests.
위의 3개중에서 Section 5.2.2 항목이 어렵습니다. requirement 는 Pipe & Fitting 은 CE 가 max 0.35 이고
Flange 는 CE 가 max 0.42 입니다. 이를 만족하려면 Flange & Flange PQR 밖에 없는데
협력업체에서는 이를 PQR 할 수 없다고 합니다.
CE 가 높은 (0.41이상) 배관자재를 구해보라고 했더니, 자재를 구하지 못하고 있습니다.
base metal chemistry control 은 위와 같이 CE(Pipe & Fitting 은 CE 가 max 0.35, Flange 는 CE 가
max 0.42) 로 관리하고 있습니다.
++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++
결론
NACE RP0472 를 적용하는데, 적용예외조항이 제가 해석한 부분이 맞는지? 그리고 "특히 base metal
chemistry control 을 하고 있다고 봐야 하는지요"
그리고 Flange & Flange PQR 이 가능한지 하는 것입니다.
필요한 PQR 자재는 2" sch 80 (5.5mm), 2" sch 160 (8.7mm), 6" sch 80 (10.97mm) 의 Carbon
Steel 및 LTCS 자재 입니다.
이 적용조항에 대한 답변이 있는 Code 또는 Standard 가 있으면 더욱더 좋겠습니다.
감사합니다.
아래는 NACE RP0472 Section 5.1 의 원본입니다.
5.1 ASME Boiler and Pressure Vessel Code, Section IX,
requires qualification of welding procedures to ensure that
room-temperature tensile strength and ductility of the
weldment meet minimum values. Welding must be
performed within the essential variables specified for the
welding process used. The ASME Boiler and Pressure
Vessel Code has no requirements for hardness testing
during procedure qualification tests. The following
practices for hardness testing during procedure
qualification tests have been developed and apply
primarily to weldments where PWHT or base material
chemistry controls are not used. The user shall specify
when this hardness testing is required and which of the
following practices are required, after reviewing the
intended service for the weldment.
이를 현장에 적용하는데, 어디까지 적용을 하는가가 관건입니다.
파란색글짜를 보시면, 적용예외사항이 나옵니다.
1) 열처리를 하는 경우와 2) base metal chemistry control 을 하지
않는 경우로 해석됩니다.
++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++
상황설명
PQR 시에 NACE RP 0472 Section 5 에 따라서 Hardness 를 하라고 해서 Hardness만을 따라 했고
(합격범위에 들었음), 기타 다른 조항은 ASME Section IX 를 따랐음.
사업주는 NACME RP 0472 Section 5에 따라서 PQR 을 다시 하라는 것입니다.
즉 Section 5.2.2 에 따라서 최대 CE 로 하라고 하고,
5.2.2 Maximum CE should not exceed the
corresponding values obtained on the test sample.
All chemical requirements should be applied to ladle
analyses, unless otherwise specified by the user.
그리고 Section 5.2.4 에 따라서 입열량을 제어하고
5.2.4 For all welding processes, the heat input
during production welding should not vary by more
than +25/-10% from the heat input used on the test
sample.
마지막으로 Section 5.2.7 에 따라 예열및 층간온도를 관리하라고 합니다.
5.2.7 Preheat and interpass temperatures used
during production welding should be greater than or
equal to that used in the welding procedure
qualification tests.
위의 3개중에서 Section 5.2.2 항목이 어렵습니다. requirement 는 Pipe & Fitting 은 CE 가 max 0.35 이고
Flange 는 CE 가 max 0.42 입니다. 이를 만족하려면 Flange & Flange PQR 밖에 없는데
협력업체에서는 이를 PQR 할 수 없다고 합니다.
CE 가 높은 (0.41이상) 배관자재를 구해보라고 했더니, 자재를 구하지 못하고 있습니다.
base metal chemistry control 은 위와 같이 CE(Pipe & Fitting 은 CE 가 max 0.35, Flange 는 CE 가
max 0.42) 로 관리하고 있습니다.
++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++++
결론
NACE RP0472 를 적용하는데, 적용예외조항이 제가 해석한 부분이 맞는지? 그리고 "특히 base metal
chemistry control 을 하고 있다고 봐야 하는지요"
그리고 Flange & Flange PQR 이 가능한지 하는 것입니다.
필요한 PQR 자재는 2" sch 80 (5.5mm), 2" sch 160 (8.7mm), 6" sch 80 (10.97mm) 의 Carbon
Steel 및 LTCS 자재 입니다.
이 적용조항에 대한 답변이 있는 Code 또는 Standard 가 있으면 더욱더 좋겠습니다.
감사합니다.
결론이 났습니다.
1. 3rd party Lab 에서 Flange 와 Pipe 의 용접후 길이를 60cm 로 하면
PQR 을 할 수 있다고 하여 쿠폰을 만들어다 주었습니다.
2. CE 가 비교적 높은 배관 (0.35 이상) 과 Flange (0.41 이상)을 용접
하였습니다.
(사업주가 승인함. Flange만으로는 적정 쿠폰 길이를 만들 수 없음.
Long weld neck flange 는 두꺼워서 QW-403.6 을 만족시키기 어려워
포기함)
3. Preheating & Interpass temperature Requirements 를 따라서 용접을
했습니다. 즉 Interpass Temperature 를 가능한 낮게 하였습니다.
시간이 많이 소요되었지요.
자재구하고 PQR 하고 결과얻기까지 2달이나 걸렸습니다.
감사합니다.
이미 질문하신 분이 답은 다 알고 있으면서 푸념을 한 것으로 이해합니다.
저런 PMC를 만나면 갑갑하지요.
그래도 궁금해 할 사람들을 위해서 간단하게 의견드립니다.
- 열처리 예외 조항은 해석이 맞습니다. 그런데, 지금 RP가 SP로 바뀌면서 해당 내용이 사라졌습니다.
- Max. CE는 원소재가 그 값을 넘지 말라는 얘기지.. 그렇게 높은 값으로 Test를 하라는 얘기가 아닙니다.
- Flange to Flange의 PQR은 억지로 시편을 만들어 볼수는 있겠으나, 그걸 가지고 무슨 Test를 할 수 있겠습니까...
우선 개정된 SP-0472를 보여주고, 전체적으로 설명을 해 주는 노력이 필요하겠습니다.
참고로 5월 셋째 주에 숭실대학교에서 NACE Code Clinic을 하루 Cource로 진행합니다.
자세한 내용은 일정이 확정되면 공지사항으로 올려드리겠습니다.