김상준
2003-10-31 18:00:04
2
317
안녕하십니까?
저희회사는 단조피팅업체인데, Stabilization(안정화)처리에
대해 궁금한 점이 있어서 이 글을 씁니다.
저희가 오스테나이트 계열의 소재인 321,347 을 구입을 하였는데,
solution(고용화)처리까지 된 상태로 구입을 하였읍니다.
그런데, 안정화처리르 해야된다고 owner쪽에서 요구를 하더라구요.
그래서 저희가 열처리를 900℃ 에서 약1 ~ 2시간을 실시하려고
하는데 냉각방법을 모르겠읍니다.
공냉을 해야 되는지 수냉을 해야되는지????
냉각방법에 따라 어떻게 소재성질이 달라지는지 ???
안정화 처리를 하는 이유가 뭔지 자세한 내용을 알고싶네요.
아시는 분 글좀 올려주세요.
1. Survey of ASTM A376-01a
para. 6.2.3; 321SS & 347SS shall be solution heat treated at min. 1900 deg.F (1040 deg.C). (Mandatory Requirement)
S.9 ; Subsequent (stabilization) heat treatment shall be done less than the solution heat treatment in para. 6.2. The stabilization heat treatment temperature shall be decided as agreed upon between the purchaser and vendor.(Supplementary Requirement)
2. Metallurgical Review and Conclusion
2.1 Stabilization heat treatment (Normally at min. 1650 deg.F = 899 deg.C) of S9 is not mandatory requirement in ASTM and ASME. Please check the client`s spec.
2.2 Rapid cooling for 321SS or 347SS in stabilization/solution heat treatment is not critical. Slow cooling is more recommended for the coarse grain practice in high temperature service.
2.3 Stabilizing effect for 321SS or 347SS can be fully obtained by stabilizing heat treatment (at min. 1650 deg.F = 899 deg.C) as well as solution heat treatment (at min. 1900 deg.F = 1040 deg.C.)
2.4 Sometimes the stabilizing heat treatment for products (not material) is required in high chloride environment in client`s spec. Please check the client`s spec.
Hope this helps,
Thomas J.C. Eun
para. 6.2.3; 321SS & 347SS shall be solution heat treated at min. 1900 deg.F (1040 deg.C). (Mandatory Requirement)
S.9 ; Subsequent (stabilization) heat treatment shall be done less than the solution heat treatment in para. 6.2. The stabilization heat treatment temperature shall be decided as agreed upon between the purchaser and vendor.(Supplementary Requirement)
2. Metallurgical Review and Conclusion
2.1 Stabilization heat treatment (Normally at min. 1650 deg.F = 899 deg.C) of S9 is not mandatory requirement in ASTM and ASME. Please check the client`s spec.
2.2 Rapid cooling for 321SS or 347SS in stabilization/solution heat treatment is not critical. Slow cooling is more recommended for the coarse grain practice in high temperature service.
2.3 Stabilizing effect for 321SS or 347SS can be fully obtained by stabilizing heat treatment (at min. 1650 deg.F = 899 deg.C) as well as solution heat treatment (at min. 1900 deg.F = 1040 deg.C.)
2.4 Sometimes the stabilizing heat treatment for products (not material) is required in high chloride environment in client`s spec. Please check the client`s spec.
Hope this helps,
Thomas J.C. Eun
공지사항
위하여 Ti(321) Nb(347)을 첨가하여 내부식성을 향상시킨 강재입니다.
2. 위의 TI,Nb를 첨가할 경우 Carbon은 Cr 탄화물을 형성하지 않고
Ti, Nb와 탄화물을 형성합니다.
이를 통하여 Carbon이 Cr과 형성하는 것을 억제합니다.
TiC/NbC는 용접시 용해되고 급냉시 TiC/NbC 가 재형성되지 않습니다.
이 경우 용접선과 평행하게 진행하는 Knife Line attack 이라는
입계부식과 는 다른 부식이 HAZ에 발생합니다.
3. 일반적으로 321/347은 고용화 열처리(Solution Annealing) 한 것으로
사용하여도 무방합니다.(1040~1060`C)
다만 321H/347H는 900+-25`C에서 안정화열처리를 하여야 합니다.
4. 이에 대한 규정은 ASTM 또는 ASME의 관련 Code를 확인하여 보시기
바라며, Stainless Steel에 대한 내용은 본 사이트의 기술문서의
Stainless Steel 관련 자료를 확인하시면 더 자세히 알 수 있습니다.