NACE MR0103에 대하여 조사를 하던중 올라온 글들이 큰 도움이 됐습니다.
하지만 제가 초보자라 질의가 생겨 올립니다.
재질은 SA516-70이고 MPS상에 NACE MR0103만 적용할것으로 적혀있고 별도의 요구사항은 전무합니다.
여기 올라온 글들을 보면 카본스틸이라 별도의 테스트가 없어도 된다고 이해가 됐는데 다른테스트를 해야되는건지 아리송해서 글을 올립니다.
답변 부탁드립니다.
하지만 제가 초보자라 질의가 생겨 올립니다.
재질은 SA516-70이고 MPS상에 NACE MR0103만 적용할것으로 적혀있고 별도의 요구사항은 전무합니다.
여기 올라온 글들을 보면 카본스틸이라 별도의 테스트가 없어도 된다고 이해가 됐는데 다른테스트를 해야되는건지 아리송해서 글을 올립니다.
답변 부탁드립니다.
I have somewhat different thoughts below.
MR (Material Requirements) is not for raw (base) materials only but for product materials as well as raw (base) materials. NACE MR0103 has the following standards for production.
- Hardness limitation for weldments (including WPS/PQR/WPQ)-i.e., RP0472 for P, No.1 carbon steel and raw (base) materials. All hardness limitations in MR0103 shall be applied to weldments as well.*
- Welding and cladding restriction for some materials
- Heat treatment procedures including PWHT for some materials
- Stamping on the metals
- Threading
- Cold forming and cold strain
Even though MR0103 has been developed from the corrosion mechanism and requirements in MR0175, all requirements in MR0103 are completely separated from those in MR0175. It means no requirements are connected between two standards.
Meanwhile in MR0103, TM0177 is not mandatory requirement (See para.1.4 in MR0103) whilst RP0472 is mandatory standard.
* For example:
When you buy the A516-70 in MR0103 service condition, do you think there is no hardness requirement for the raw material? If you do not have a specific requirement (or require max. 200 BHN) for the hardness value of base metal, can you meet the 200 BHN on the weldments of metal? I believe it is not easy to meet the requirement. Therefore I would like to recommend the following hardness control (max hardness of the base metal), but the responsibility for final products is yours.
- Base metal with PWHT : max (200 minus 10 or 20 per thickness and repair times) BHN
- Base metal without PWHT : max (200 minus 30 or 40 per thickness and repair times) BHN
In general, these requirements may not be impact of cost or delivery, but it may relieve all risk in your design engineering.
Please be aware the hardness measuring is one of the tests.
MR (Material Requirements) is not for raw (base) materials only but for product materials as well as raw (base) materials. NACE MR0103 has the following standards for production.
- Hardness limitation for weldments (including WPS/PQR/WPQ)-i.e., RP0472 for P, No.1 carbon steel and raw (base) materials. All hardness limitations in MR0103 shall be applied to weldments as well.*
- Welding and cladding restriction for some materials
- Heat treatment procedures including PWHT for some materials
- Stamping on the metals
- Threading
- Cold forming and cold strain
Even though MR0103 has been developed from the corrosion mechanism and requirements in MR0175, all requirements in MR0103 are completely separated from those in MR0175. It means no requirements are connected between two standards.
Meanwhile in MR0103, TM0177 is not mandatory requirement (See para.1.4 in MR0103) whilst RP0472 is mandatory standard.
* For example:
When you buy the A516-70 in MR0103 service condition, do you think there is no hardness requirement for the raw material? If you do not have a specific requirement (or require max. 200 BHN) for the hardness value of base metal, can you meet the 200 BHN on the weldments of metal? I believe it is not easy to meet the requirement. Therefore I would like to recommend the following hardness control (max hardness of the base metal), but the responsibility for final products is yours.
- Base metal with PWHT : max (200 minus 10 or 20 per thickness and repair times) BHN
- Base metal without PWHT : max (200 minus 30 or 40 per thickness and repair times) BHN
In general, these requirements may not be impact of cost or delivery, but it may relieve all risk in your design engineering.
Please be aware the hardness measuring is one of the tests.
공지사항
그런데, 원론적인 얘기로 들어가면, MR은 Material Requirement의 약자로서 원소재에 대한 일련의 Requirement를 나열한 것입니다.
그럼 그런 소재에 대한 평가는 어떻게 하는가?
NACE Code에는 TM이라는 것이 있습니다.
Test Method를 의미하는 것으로서 일련의 기계적 시험 및 부식성 평가를 수행하도록 규정하고 있지요.
MR-0103에도 보면 원소재와 관련하여 두가지 Code를 언급하고 있습니다.
MR-0175와 TM-0177이 그것 입니다.
이중에 TM-0177은 부식환경하에서 직접 기계적 시험을 수행하는 일련의 Test를 언급하고 있습니다.
그렇다면 Mill Maker에서는 매번 이런 시험을 통해 원자재를 검증하고 평가해서 그 결과를 Mill Certificate에 표기해야 하는가?
역시 원론적인 입장에서는 그렇게 해야 하는 것이 맞습니다.
하지만, NACE MR-0175 후반부 및 NACE Code 전반을 잘 읽어 보면 이러이러한 재질은 굳이 개별적인 Test를 TM-0177에 따라 실시할 필요없이 그냥 각 제조자의 관리기준에 따라 NACE에서 얘기하는 경도 등의 기준만을 만족하는 수준에서 생산하여 공급하면 된다고 되어 있습니다.
즉, 매번 Test하기가 어려우니, 그냥 이러 이러한 재질은 NACE에서 인정하는 것이니 그냥 편하게 써라... 다만 경도나 열처리 등의 추가 사항은 꼭 지켜라... 이렇게 규정되어 있는 것이지요.
따라서, 지금 원소재를 구매하여 사용하는 제조자의 입장에서는 그냥 편하게 A516-60/70을 구매하여 사용하면 됩니다.
NACE MR-0103을 적용하는 한, 별도의 Test를 고려하지 않아도 됩니다.