L-grade의 용접봉은 고온에서 Allowable Stress가 없어서 사용에 제한이 있습니다. 그래서 고온에서는 Nb가 함유된 용접봉을 사용하여 고온 강도와 함께 입게 예민화에 대한 대안으로 사용합니다. 이들 재질의 Allowable Stress 값을 찾아 보시면 무슨 애기인지 바로 아실 수 있습니다.

ER316L This classification is the same as ER316, except for the carbon content. Low carbon (0.03 percent maximum) in this filler metal reduces the possibility of intergranular chromium carbide precipitation and thereby increases the resistance to intergranular corrosion without the use of stabilizers such as niobium or titanium. This filler metal is primarily used for welding low-carbon molybdenum-bearing austenitic alloys. This low-carbon alloy, however, is not as strong at elevated temperature as the niobium-stabilized alloys or Type ER316H. ER318 This composition is identical to ER316, except for the addition of niobium. Niobium provides resistance to intergranular chromium carbide precipitation and thus increased resistance to intergranular corrosion. Filler metal of this classification is used primarily for welding base metals of similar composition.

인장강도 측면에서 보면, 316Ti의 최소요구인장강도가 75 ksi(515 MPa)입니다. 316L은 70(485) 입니다. 용접봉 318은 UTS가 550 MPa이네요. 화학조성은 C(Carbon)빼고는 316L과 318이 비슷합니다. PQ Test를 생각하면, 318을 적용하는 것이 나을 듯 합니다. 위와 같이 생각을 했는데, 표를 찾아보니, 어떤 표에서는 317L, 316L, 316Ti 용접의 용접봉을 316L을 적용하라고 되어 있네요. 어떤 자료에서는 316Ti 용접봉으로 316L과 318을 둘다 추천하고 있고, 인장강도가 요구하는 최소값이상으로 되면, 두 용접봉 모두 사용이 가능한 것으로 생각됩니다.